CNT/fluoropolymer coating composition

ABSTRACT

Exemplary embodiments provide nanotube-containing coating compositions and methods for making and using the coating compositions. In an exemplary embodiment, the coating composition can include a plurality of nanotubes (e.g., carbon nanotubes (CNTs)) dispersed stably and uniformly in a polymer matrix containing fluoropolymers. The coating composition can further include stabilizers to allow a stable and/or uniform dispersion of the plurality of nanotubes in the fluoropolymers. The nanotube coating composition can be coated on an article surface to improve mechanical robustness, and electrical and thermal conductivity of the coated article. The coated article can be used as, for example, a fuser member, a fixing member, a pressure roller, or a release agent donor member in an electrostatographic printing machine or process.

FIELD OF THE INVENTION

This invention relates generally to coating compositions and methods formaking and using the coating compositions and, more particularly, tonanotube-containing coating compositions and methods for making andcoating the nanotube-containing coating compositions used forelectrostatographic devices and processes.

BACKGROUND OF THE INVENTION

In electrophotography (also known as xerography, electrophotographicimaging or electrostatographic imaging), the surface of an imagingmember (e.g., photoreceptor) is first uniformly electrostaticallycharged. The imaging member contains a photoconductive insulating layeron a conductive layer and is then exposed to a pattern of activatingelectromagnetic radiation, such as a light. Charge generated by thephotoactive pigment moves under the force of the applied field. Themovement of the charge through the photoreceptor selectively dissipatesthe charge on the illuminated areas of the photoconductive insulatinglayer while leaving behind an electrostatic latent image. Thiselectrostatic latent image is then developed to form a visible image bydepositing oppositely charged particles on the surface of thephotoconductive insulating layer.

The resulting visible image is then transferred from the imaging memberdirectly or indirectly (such as by a transfer or other member) to aprint substrate, such as a transparency or paper sheet. The imagingprocess may be repeated many times with reusable imaging members. Thevisible toner image is therefore transferred on the print substrate andis usually fixed or fused to form permanent images since the visibletoner image is in a loose powdered form and can be easily disturbed ordestroyed. The use of thermal energy for fixing toner images onto asupport member is well known. In order to fuse electroscopic tonermaterial onto a support surface permanently by heat, it is necessary toelevate the temperature of the toner material to a point at which theconstituents of the toner material coalesce and become tacky. Thisheating causes the toner to flow to some extent into the fibers or poresof the support member. Thereafter, as the toner material cools,solidification of the toner material causes the toner material to befirmly bonded to the support.

Several approaches to thermal fusing of electroscopic toner images havebeen described in the prior art. These methods include providing theapplication of heat and pressure substantially concurrently by variousmeans: a roll pair maintained in pressure contact; a belt member inpressure contact with a roll; and the like. Heat may be applied byheating one or both of the rolls, plate members or belt members. Thefusing of the toner particles takes place when the proper combination ofheat, pressure and contact time is provided. The balancing of theseparameters to bring about the fusing of the toner particles is wellknown in the art, and they can be adjusted to suit particular machinesor process conditions.

Fuser and fixing rolls or belts may be prepared by applying one or morelayers to a suitable substrate. Typically, fuser and fixing rolls orbelts include a surface layer for good toner releasing. Cylindricalfuser and fixer rolls may be prepared by applying a silicone elastomeror fluoroelastomer to serve as a releasing layer. Known fuser surfacecoatings also include crosslinked fluoropolymers such as VITON-GF®(DuPont) used in conjunction with a release fluid.

Another type of surface layer materials includes fluororesin such aspolytetrafluoroethylene (PTFE), perfluoroalkylvinylether copolymer (PFA)and the like. This type of materials are desired for oil-less fusing,namely, no release fluid being required. Specifically, the Teflonsurface enables oil-less fusing and the silicone layer providesconformability which enables rough paper fix, low mottle and gooduniformity. Problems arise, however, due to insufficient mechanicalrobustness of the Teflon surface coatings, e.g., cracking and abrasion,which results in short operating life of the fuser. In addition, thereis a need for electrical conductivity to dissipate the electrostaticbuilt up during fusing process.

Carbon nanotubes (CNTs) possess exceptional mechanical properties andsuperior electric and thermal properties and can be used asreinforcement for structural composites. It is therefore desired toemploy carbon nanotubes for the fuser. However, due to the uniquestructural features of CNTs, e.g., the nanometer size and the highaspect ratio, CNTs tend to stay aggregated in the resulting composite.

Thus, there is a need to overcome these and other problems of the priorart and to provide coating compositions and methods for making and usingthe coating compositions where CNTs can be stably and uniformlydispersed in the composition.

SUMMARY OF THE INVENTION

According to various embodiments, the present teachings include acoating composition. The coating composition can include afluoropolymer, a plurality of nanotubes dispersed in a media; and astabilizer mixed with the plurality of nanotubes. The stabilizer can beused to allow a stable dispersion of the plurality of nanotubes in themedia and in the fluoropolymer.

According to various embodiments, the present teachings also include acoated article. The coated article can include a substrate, and a coatedlayer. The coated layer can be disposed over the substrate and formedfrom applying a coating composition to the substrate. The coatingcomposition can include a fluoropolymer, a plurality of nanotubesdispersed in a media; and a stabilizer mixed with the plurality ofnanotubes. The stabilizer can be used to allow a stable dispersion ofthe plurality of nanotubes in the media and in the fluoropolymer.

Additional objects and advantages of the invention will be set forth inpart in the description which follows, and in part will be obvious fromthe description, or may be learned by practice of the invention. Theobjects and advantages of the invention will be realized and attained bymeans of the elements and combinations particularly pointed out in theappended claims.

It is to be understood that both the foregoing general description andthe following detailed description are exemplary and explanatory onlyand are not restrictive of the invention, as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and constitute apart of this specification, illustrate several embodiments of theinvention and together with the description, serve to explain theprinciples of the invention.

FIG. 1 depicts a schematic showing an exemplary stabilizer polymer inaccordance with the present teachings.

FIG. 2 depicts an exemplary method for forming a stable nanotube-coatingcomposition in accordance with the present teachings.

FIG. 3 depicts another exemplary method for forming a stablenanotube-coating composition in accordance with the present teachings.

FIGS. 4A-4B depict exemplary coated articles having an exemplary coresubstrate in accordance with the present teachings.

FIGS. 5A-5B are schematics showing exemplary coated layers used as theoutermost layer of the coated articles of FIGS. 4A-4B formed by themethod of FIG. 2 in accordance with the present teachings.

FIGS. 6A-6B are schematics showing exemplary coated layers used as theoutermost layer of the coated articles of FIGS. 4A-4B formed by themethod of FIG. 3 in accordance with the present teachings.

FIG. 7A depicts exemplary as-received carbon nanotubes in accordancewith the present teachings.

FIG. 7B depicts an exemplary nanotube-composition coated layer inaccordance with the present teachings.

FIG. 8 depicts a surface resistivity for an exemplary CNT/fluoropolymercoated layer in accordance with the present teachings.

DESCRIPTION OF THE EMBODIMENTS

Reference will now be made in detail to the present embodiments(exemplary embodiments) of the invention, an example of which isillustrated in the accompanying drawings. Wherever possible, the samereference numbers will be used throughout the drawings to refer to thesame or like parts. In the following description, reference is made tothe accompanying drawings that form a part thereof, and in which isshown by way of illustration specific exemplary embodiments in which theinvention may be practiced. These embodiments are described insufficient detail to enable those skilled in the art to practice theinvention and it is to be understood that other embodiments may beutilized and that changes may be made without departing from the scopeof the invention. The following description is, therefore, merelyexemplary.

While the invention has been illustrated with respect to one or moreimplementations, alterations and/or modifications can be made to theillustrated examples without departing from the spirit and scope of theappended claims. In addition, while a particular feature of theinvention may have been disclosed with respect to only one of severalimplementations, such feature may be combined with one or more otherfeatures of the other implementations as may be desired and advantageousfor any given or particular function. Furthermore, to the extent thatthe terms “including”, “includes”, “having”, “has”, “with”, or variantsthereof are used in either the detailed description and the claims, suchterms are intended to be inclusive in a manner similar to the term“comprising As used herein, the term “one or more of” with respect to alisting of items such as, for example, A and B, means A alone, B alone,or A and B. The term “at least one of” is used to mean one or more ofthe listed items can be selected.

Notwithstanding that the numerical ranges and parameters setting forththe broad scope of the invention are approximations, the numericalvalues set forth in the specific examples are reported as precisely aspossible. Any numerical value, however, inherently contains certainerrors necessarily resulting from the standard deviation found in theirrespective testing measurements. Moreover, all ranges disclosed hereinare to be understood to encompass any and all sub-ranges subsumedtherein. For example, a range of “less than 10” can include any and allsub-range between (and including) the minimum value of zero and themaximum value of 10, that is, any and all sub-ranges having a minimumvalue of equal to or greater than zero and a maximum value of equal toor less than 10, e.g., 1 to 5. In certain cases, the numerical values asstated for the parameter can take on negative values. In this case, theexample value of range stated as “less than 10” can assume values asdefined earlier plus negative values, e.g. −1, −1.2, −1.89, −2, −2.5,−3, −10, −20, −30, etc.

Exemplary embodiments provide nanotube-containing coating compositionsand methods for making and using the coating compositions. In anexemplary embodiment, the coating composition can include a plurality ofnanotubes (e.g., carbon nanotubes (CNTs)) dispersed stably and uniformlyin a polymer matrix containing fluoropolymers. The coating compositioncan further include stabilizers to allow a stable and/or uniformdispersion of the plurality of nanotubes in the fluoropolymers Thenanotube coating composition can be coated on an article surface toimprove mechanical robustness, and electrical and thermal conductivityof the coated article. The coated article can be used in anelectrostatographic printing device or process, e.g., to enableelectrostatic dissipation and surface heat uniformity The coated articlecan be used as, such as, for example, a fuser member, a fixing member, apressure roller, or a release agent donor member.

As used herein and unless otherwise specified, the term “nanotubes”refers to elongated materials (including organic and inorganicmaterials) having at least one minor dimension, for example, width ordiameter, about 100 nanometers or less. Although the term “nanotubes” isreferred to throughout the description herein for illustrative purposes,it is intended that the term also encompass other elongated structuresof like dimensions including, but not limited to, nanoshafts,nanopillars, nanowires, nanorods, and nanoneedles and their variousfunctionalized and derivatized fibril forms, which include nanofiberswith exemplary forms of thread, yarn, fabrics, etc.

In various embodiments, the nanotubes can have an inside diameter and anoutside diameter. For example, the inside diameter can range from about0.5 to about 20 nanometers, while the outside diameter can range fromabout 1 to about 80 nanometers. The nanotubes can have an aspect ratio,e.g., ranging from about 1 to about 10000.

The term “nanotubes” can also include single wall nanotubes such assingle wall carbon nanotubes (SWCNTs), multi-wall nanotubes such asmulti-wall carbon nanotubes (MWCNTs), and their various functionalizedand derivatized fibril forms such as nanofibers. The term “nanotubes”can further include carbon nanotubes including SWCNTs and/or MWCNTs.Furthermore, the term “nanotubes” can include modified nanotubes fromall possible nanotubes described thereabove and their combinations. Themodification of the nanotubes can include a physical and/or a chemicalmodification.

The nanotubes can have various cross sectional shapes, such as, forexample, rectangular, polygonal, oval, or circular shape. Accordingly,the nanotubes can have, for example, cylindrical 3-dimensional shapes.

The nanotubes can be formed of conductive or semi-conductive materials.In some embodiments, the nanotubes can be obtained in low and/or highpurity dried paper forms or can be purchased in various solutions. Inother embodiments, the nanotubes can be available in the as-processedunpurified condition, where a purification process can be subsequentlycarried out.

The nanotubes can provide exceptional and desired functions, such as,mechanical, electrical (e.g., conductivity), and thermal (e.g.,conductivity) functions to the coating composition and the coatedarticle. In addition, the nanotubes can be modified/functionalizednanotubes with controlled and/or increased mechanical, electrical orthermal properties through various physical and/or chemicalmodifications.

The nanotubes, such as carbon nanotubes (CNTs), can be dispersed in amedia first in order to form the coating composition The media used forthe plurality of nanotubes can be a liquid including, but not limitedto, water, alcohols, aliphatic hydrocarbons of, e.g., from C5 to aboutC18, aromatic hydrocarbons of, e.g., from C6 to C18, dioxanes, ethers,ketones, amides and mixtures thereof. The nanotubes can further bedispersed in the polymer matrix, e.g., fluoropolymers, having a weightloading of, for example, about 0.01% to about 20% of the fluoropolymer.

As used herein, the term “fluoropolymer” refers to a polymer that has amonomeric repeat unit selected from the group consisting oftetrafluoroethylene, perfluoro(methyl vinyl ether), perfluoro(propylvinyl ether), perfluoro(ethyl vinyl ether), vinylidene fluoride,hexafluoropropylene, and mixtures thereof. The fluoropolymers caninclude linear or branched polymers, and/or cross-linkedfluoroelastomers. Examples of fluoropolymer can include apoly(vinylidene fluoride), or a copolymer of vinylidene fluoride withanother monomer selected from the group consisting ofhexafluoropropylene, tetrafluoroethyelene, and a mixture thereof.

Other suitable fluoropolymers can include fluororesins andfluoroelastomers. Examples of suitable fluororesin can includepolytetrafluoroethylene, copolymer of tetrfluoroethylene andhexafluoropropylene, copolymer of tetrafluoroethylene andperfluoro(propyl vinyl ether), copolymer of tetrafluoroethylene andperfluoro(ethyl vinyl ether), copolymer of tetrafluoroethylene andperfluoro(methyl vinyl ether).

Examples of suitable fluoroelastomers can include, but are not limitedto, i) copolymers of vinylidenefluoride and hexafluoropropylene; ii)terpolymers of vinylidenefluoride, hexafluoropropylene andtetrafluoroethylene; and iii) tetrapolymers of vinylidenefluoride,hexafluoropropylene, tetrafluoroethylene and a cure site monomer. Forexample, specifically, suitable fluoropolymers can be those described indetail in U.S. Pat. Nos. 5,166,031, 5,281,506, 5,366,772, 5,370,931,4,257,699, 5,017,432 and 5,061,965, the entire disclosures each of whichare incorporated by reference herein in their entirety. As describedtherein these fluoropolymers, particularly from the class of copolymersof vinylidenefluoride and hexafluoropropylene; terpolymers ofvinylidenefluoride, hexafluoropropylene and tetrafluoroethylene; andtetrapolymers of vinyl idenefluorid e, hexafluoro propylene,tetrafluoroethylene and cure site monomer, can be known commerciallyunder various designations as Teflon® PFA(polyfluoroalkoxypolytetrafluoroethylene), Teflon® PTFE(polytetrafluoroethylene), Teflon® FEP (fluorinated ethylenepropylenecopolymer), Viton A® (copolymers of hexafluoropropylene (HFP) andvinylidene fluoride (VDF or VF2)), Viton ®-B, (terpolymers oftetrafluoroethylene (TFE), vinylidene fluoride (VDF) andhexafluoropropylene (HFP)); and Viton ®-GF, (tetrapolymers includingTFE, VF2, HFP), as well as Viton E®, Viton E 60C®, Viton E430®, Viton910®, Viton GH® and Viton GF®. The Teflon® and Viton® designations areTrademarks of E.I. DuPont de Nemours, Inc.

The cure site monomer can be, for example,4-bromoperfluorobutene-1,1,1-dihydro-4-bromoperfluorobutene-1,3-bromoperfluoropropene-1,1,1-dihydro-3-bromoperfluoropropene-1,or any other suitable, known cure site monomer commercially availablefrom DuPont. Other commercially available fluoropolymers can include,for example, Fluorel 2170®, Fluorel 2174®, Fluorel 2176®, Fluorel 2177®and Fluorel LVS 76®, Fluorel® being a Trademark of 3M Company.Additional commercially available materials can include Aflas® apoly(propylene-tetrafluoroethylene) and Fluorel II® (LII900) apoly(propylene-tetrafluoroethylenevinylidenefluoride) both alsoavailable from 3M Company, as well as the Tecnoflons identified asFor-60KIR®, For-LHF®, NM®, For-THF®, For-TFS®, TH®, and TN505®,available from Montedison Specialty Chemical Company. In certainembodiments, the fluoropolymer can be PFA Teflon®, Viton GF® or VitonGH®.

Because of a large surface area to volume ratio, nanotubes can have atendency to clump together or agglomerate, and as such may not beamenable to processing into nanotube/polymer composites. One or morestabilizers can be used to facilitate the stable and uniform dispersionof nanotubes in the polymer to form the disclosed nanotube composite.

As used herein the term “stabiizer” refers to any functional materialadmixed with the plurality of nanotubes and/or the nanotube coatingcomposition so as to allow the nanotubes and/or other possible particlessuch as inorganic filler particles to be substantially non-agglomeratedand to be substantially uniformly-dispersed in the nanotube media or thefluoropolymer.

In various embodiments, the stabilizer can include a material selectedfrom the groups consisting of polymeric amines, polymeric acids,conjugated polymers and natural gum materials. In other embodiments, thestabilizer can be a material selected from the groups consisting ofpolyallylamine, polyethylenimine, poly(diallyldimethylammoniumchloride), poly(allylamine hydrochloride), and the mixture thereof. Instill other embodiments, the stabilizer can include a material chosenfrom poly(acrylic acid), poly(3,4-ethylenedioxythiophene),poly(3,4-ethylenedioxythiophene) complexes with a polymeric acid, GumArobic, and/or chitosan.

For purposes of this application, the term “dispersion” refers to anysystem that include one substance being in another, e.g., one substancedissolving in another, or particles or other substance suspending orscattering in a fluid. Thus, the term “dispersion” can also be referredto herein as “solution”, “suspension”, “latex” or “emulsion”. In variousembodiments, the dispersion that involves one or more materials of astabilizer, a fluoropolymer, nanotubes or fillers for the disclosedcoating compositions, can be controlled having a pH value. For example,to adjust the pH value, a variety of organic or inorganic acids oralkalines can be used including, but not limited to, acetic acid,sulfonic acid, hydrochloric acid, sodium hydroxide, or any othersuitable acids or alkalines known to one of ordinary skill in the art.In various embodiments, the pH value can range from about 2 to about 11.In an additional example, the pH value can be about 3 to about 10.Further embodiments can include a pH value of about 5 to about 9.

In an exemplary embodiment, the “stabilize” can include dual structurefunctionality. For example, the stabilizer can include a functionalamino-group, which can be partially neutralized in a form of —NH₂ andcan also be partially electrostatic or ionic in a form of —NH³⁺ in thenanotube-containing dispersion, depending on the pH value of thedispersion.

FIG. 1 depicts a schematic showing an exemplary stabilizer polymerhaving dual structure amino-functional group in accordance with thepresent teachings. Specifically, the exemplary stabilizer polymer can bea partially neutralized polyallylamine that contains the amino-dualstructure functionality including neutralized amino groups (—NH₂) (see105 in FIG. 1) and amines, e.g., ammonium salt (—NH3⁺X⁻) (see 107 inFIG. 1) in an acidic condition. In various embodiments, the exemplarypolyallyamine can have a molecular weight ranging from about 300 toabout 100,000.

FIGS. 2-3 depict exemplary methods 200 and 300 for forming a stablenanotube coating composition in accordance with the present teachings.Note that while the exemplary method 200 or 300 is illustrated anddescribed below as a series of acts or events, it will be appreciatedthat the present invention is not limited by the illustrated ordering ofsuch acts or events. For example, some acts may occur in differentorders and/or concurrently with other acts or events apart from thoseillustrated and/or described herein, in accordance with the presentteachings. In addition, not all illustrated steps may be required toimplement a methodology in accordance with the present teachings.

In various embodiments, ultrasonic energy sources, such ashigh-intensity ultrasonic processors, can be used to sonicate thedispersion as desired during any stage(s) of forming the nanotubecoating composition to facilitate the dispersing of the stabilizer, thenanotubes, the inorganic filler particles and/or the fluoropolymer. Inaddition, pH value of the dispersion can be adjusted to maintain adesired value during any stage(s) of forming the nanotube coatingcomposition.

Referring back to FIG. 2, at 210, a stabilizer solution can be formed.The stabilizer solution can include one or more stabilizers, such as,polyallylamine, in a suitable solvent, such as water. In an exemplaryembodiment, hydrochloride acid (HCl) can be used to control the pH valueof the stabilizer solution when polyallylamine is used.

In FIG. 2 at 220, fluoropolymer(s) can be provided in a form of colloiddispersion, latex, suspension, or a mixture thereof. For example, thefluoropolymer can be in a form of particle dispersion with an averageparticle size ranging from about 10 to about 5000 nanometers. In anexemplary embodiment, the fluoropolymer can include a mixture of smallparticles with average particle size ranging from about 50 to about 500nanometers, and large particles with average particle size ranging fromabout 1 to about 50 micrometers.

In FIG. 2 at 230, a nanotube coating composition can be formed by mixingthe nanotubes (e.g., CNTS) in a media, the stabilizer solution, and thefluoropolymer emulsion/suspension together. In one embodiment, thenanotubes in the media can be firstly mixed with the stabilizer solutionand then mixed with the fluoropolymer emulsion In another embodiment,the nanotubes in the media can be mixed with the mixture of thestabilizer solution with the provided fluoropolymer emulsion. In afurther embodiment, the nanotubes in the media can be firstly mixed withthe fluoropolymer emulsion and then mixed with the stabilizer solution

Fillers can often be used in polymer formulations as reinforcingparticles to improve the hardness and wear resistance. In variousembodiments, fillers, such as inorganic particles, can be used to formthe nanotube coating composition. For example, the inorganic particlescan be dispersed in a media, such as water, to form a filler suspension.In an exemplary embodiment, the filler suspension can be prepared bysonication of inorganic particles in the presents of surface treatmentagents such as silanes in water. In various embodiments, the inorganicparticles can include, but are not limited to, metal oxides, non-metaloxides, metals, or other suitable particles. Specifically, the metaloxides can include, for example, silicon oxide, aluminum oxide, chromiumoxide, zirconium oxide, zinc oxide, tin oxide, iron oxide, magnesiumoxide, manganese oxide, nickel oxide, copper oxide, antimony pentoxide,indium tin oxide, and mixtures thereof. The non-metal oxides caninclude, for example, boron nitride, silicon carbides (SiC) and thelike. The metals can include, for example, nickel, copper, silver, gold,zinc, iron and the like. In various embodiments, other additives knownto one of ordinary skill in the art can also be included in the nanotubecoating composition.

FIG. 3 depicts another exemplary nanotube coating composition containingfiller materials and a method for making such suspension in accordancewith the present teachings.

As shown in FIG. 3, at 315, a filler suspension can be preparedcontaining the inorganic particles as disclosed herein in a watersolvent, for example. At 330, the filler suspension formed at 315 canthen be mixed with the nanotubes, the stabilizer solution formed at 210and the fluoropolymer dispersion formed at 220 to form the disclosedcoating composition suspension. In various embodiments, the formation ofthe nanotube suspension at 210 and the formation of the fluoropolymersuspension at 220 can be similar as that described in FIG. 2.

In an exemplary embodiment, the disclosed coating composition caninclude, e.g., fluoropolymer latex particles of about 10 to 50 percentby weight of total coating composition; carbon nanotubes of about 0.1 toabout 10 percent by weight of total coating composition, polyallyamineof about 0.1 to about 10 percent by weight of total coating composition;water as media of about 50 to about 90 percent by weight of totalcoating composition; and optionally filler(s) of about 0.5 to 10 percentby weight of total coating composition.

In various embodiments, the nanotube coating composition formed as shownin FIGS. 2-3 can be, for example, a stable and uniform CNT/PFA aqueousdispersion that has a suitable shelf life, and can be “coated” onto anarticle surface as a coated layer to form a coated article. The coatedarticle can be used as, for example, a fuser member, a fixing member, apressure roller, and/or a release agent donor member in anelectrostatographic printing device and process.

The article surface to be coated can include a substrate for allpossible members/rollers described thereabove. The substrate can be in aform including, but not limited to, a belt, plate, sheet, and/orcylindrical drum. In various embodiments, the substrate to be coated caninclude a wide variety of materials, such as, for example, metals, metalalloys, rubbers, glass, ceramics, plastics, or fabrics. For example, themetals used can include aluminum, anodized aluminum, steel, nickel,copper, and mixtures thereof, while the plastics used can includepolyimides, polyester, polyetheretherketone (PEEK), poly(aryleneether)s, polyamides and mixtures thereof. In various embodiments, one ormore functional layers can be disposed between the substrate and thecoated layer.

Various coating techniques can be applied to form the disclosednanotube-composite coated article. As used herein, the term “coatingtechnique” refers to a technique or a process for applying, forming, ordepositing the coating composition on a material or a surface.Therefore, the term “coating” or “coating technique” is not particularlylimited in the present teachings, and dip coating, painting, brushcoating, roller coating, pad application, spray coating, spin coating,casting, or flow coating can be employed. For example, the nanotubecoating composition can be coated on a piece of silicon wafer byspray-coating with an air-brush.

After the nanotube coating composition is coated on the desired articlesurface, a drying process can be performed. For example, the coatedarticle can be baked at a temperature of about 200° C. or higher, suchas about 200° C. to about 400° C. in some cases, for a certain timelength. In an exemplary embodiment, the coated article can be dried at350° C. for about 20 minutes followed by a drying at 360° C. for about10 minutes. Alternatively, the drying process can include a vacuum oven.Regardless of the manner in which the coating is formed, each driedcoating layer can have a thickness. In various embodiments, the coatingand drying process can be repeated as desired to achieve a requiredthickness, for example, ranging from about 5 micron to about 50 micron,depending on the specific application of the coated article.

In one embodiment for preparing the coated article, nanotubes such ascarbon nanotubes (CNTs), can be added in a solution containingpoly(allyamine), followed by a sonication process in a suitable pHenvironment. Such dispersion can then be mixed with fluoropolymer (e.g.,Teflon PFA) emulsion to form a stable nanotube coating composition usinga sonication process. Uniform coating can then be achieved by, e.g.,spray-coating of the CNT/PFA dispersion onto an article surface,followed by baking the coated article at high temperatures, e.g., 20minutes at 351° C., then 10 minutes at 360° C.

In another embodiment for preparing the coated article, exemplary CNTscan be admixed with poly(allyamine) solution. A stable and uniformCNT/PFA dispersion, e.g., in aqueous media, can be achieved by a furthermixing with the exemplary PFA emulsion. Inorganic particles can then besurface-treated in an aqueous media and combined with the CNT/PFAdispersion to prepare filler-containing nanotube coating composition.Note that, during the dispersion preparation, sonication can be used asdesired and pH value of the dispersion can be maintained. In anexemplary embodiment, a stable and uniform dispersion containing CNT,PFA and SiC can be prepared and be spray-coated onto an article surface,followed by a baking process at high temperatures, e.g., at about 351°C. for about 20 minutes, then at about 360° C. for about 10 minutes.

FIGS. 4A-4B depict exemplary coated articles 400A-B having an exemplarycore substrate 410 in accordance with the present teachings. It shouldbe readily apparent to one of ordinary skill in the art that the devices400A-B depicted in FIGS. 4A-4B represent generalized schematicillustrations and that other layers/substrates can be added or existinglayers/substrates can be removed or modified.

The coated articles 400 A-B can be fuser rollers with one or morefunctional layers 420 and/or 430 formed on the core substrate 410. Invarious embodiments, the core substrate 410 can take the form of acylindrical tube or a solid cylindrical shaft. One of ordinary skill inthe art will understand that other substrate forms, e.g., a beltsubstrate, can be used to maintain rigidity, structural integrity of thecoated article.

As shown, the outermost layers 430 in FIG. 4A, and in FIG. 4B can be acoated layer formed from the disclosed nanotube coating composition(e.g., formed from the method 200 in FIG. 2 or the method 300 in FIG.3). The coating composition coated layer can be formed directly on thesubstrate surface 410 (see 430 in FIG. 4A) or can be formed on afunctional layer 420 that is formed on the substrate surface 410 (see430 in FIG. 4B). For example, the fuser roll can be in a 2-layerconfiguration having a compliant layer 420, such as a silicone rubberlayer having a thickness of, e.g., about 1 mm. to about 5 mm, disposedbetween the coated outermost layer 430 and the core substrate 410, suchas a metal used in the related art. In various embodiments, the coatedoutermost layer 430 can have a thickness of from about 5 microns toabout 50 microns.

FIGS. 5A-5B are schematics showing exemplary coated coating compositionlayers, e.g., the outermost layers 430 of FIGS. 4A-4B, formed by themethod 200 of FIG. 2 in accordance with the present teachings. As shownin FIGS. 5A-5B, although the plurality of nanotubes 510 is depictedhaving a consistent size in FIGS. 5A-5B, one of ordinary skill in theart will understand that the plurality of nanotubes 510 can havedifferent sizes, for example, different lengths, widths and/ordiameters. In addition, it should be readily apparent to one of ordinaryskill in the art that coated layer depicted in FIGS. 5A-5B represents ageneralized schematic illustration and that othernanotubes/dopants/layers can be added or existingnanotubes/dopants/layers can be removed or modified.

In FIG. 5A, the plurality of nanotubes 510, such as CNTs, can bedispersed uniformly throughout an exemplary fluoropolymer matrix 520.For example, this distribution can include bundled nanotubes 510dispersed uniformly but with random tangles throughout the polymermatrix 520 of the coated layer 430.

In FIG. 5B, the plurality of nanotubes 510 can be dispersed uniformlyand spatially-controlled, for example, be aligned or oriented at certaindirections, throughout the polymer matrix 520 of the coated layer 430by, for example, use of a magnetic field.

FIGS. 6A-6B are schematics showing exemplary coated coating compositionlayers, e.g., the outermost layers 430 of FIGS. 4A-4B, formed by themethod 300 of FIG. 3 in accordance with the present teachings. Ascompared with the coated layer shown in FIGS. 5A-5B, the coated layer inFIGS. 6A-6B can further include a plurality of fillers 625 along withthe plurality of nanotubes 510, which are stably and uniformly dispersedin the fluoropolymer 520. The plurality of fillers 625 can include, suchas, for example, aluminum oxide, chromium oxide, zirconium oxide, zincoxide, tin oxide, iron oxide, magnesium oxide, manganese oxide, nickeloxide, copper oxide, antimony pentoxide, indium tin oxide, boronnitride, silicon carbides, nickel, copper, silver, gold, zinc, or iron.

FIGS. 7A-7B depict a comparison between as-received carbon nanotubes(see FIG. 7A) and an exemplary coated coating composition layer (seeFIG. 7B) containing CNTs in the fluoropolymer PFA matrix using astabilizer polyallylamine in accordance with the present teachings. Ascompared with the as-received nanotubes in FIG. 7A, FIG. 7B indicatesthat the nanotubes can be uniformly dispersed within the coated layer.

In various embodiments, the coated coating composition layer shown inFIGS. 4-7 can provide desired electrical, mechanical, and thermalproperties for using in the electrostatographic printing devices andprocesses For example, FIG. 8 shows a surface resistivity result for anexemplary CNT/PFA coated layer in accordance with the present teachings.In this example, the CNT/PFA coating can be formed on a silicon waferand can have about 2 wt % CNT loading in the PFA matrix. As shown, thesurface resistivity of the coated layer can be decreased dramatically(see curve 830), as compared with the control sample that only containsPFA but without CNTs (see curve 805). That is, the surface conductivityof the coated CNT/PFA layer can be dramatically increased due to the useof nanotubes. In various embodiments, the disclosed coated layer canprovide a surface resistivity of about 10⁸ Ω/sq or less.

EXAMPLES Example 1 Mixing of CNTs with Polyallylamine Stabilizer

A polyallylamine stabilizer solution was prepared by dissolving about0.05 gram polyallylamine in about 5 g deionized water. About 0.1 gram ofCNTs was then added into the prepared polyallylamine solution, followedby a sonication with a high power sonicator for about 1 min at 60%output. About 1 mL of 1 N HCl solution was added into theCNT/polyallylamine dispersion which was sonicated for 1 min again. Theresulting CNT/polyallylamine dispersion was observed to be uniformlycoated on a piece of glass slide.

Example 2 Preparation of CNT/PFA Dispersion

About 1 gram of the mixture of CNT/polyallylamine prepared from example1 was further mixed with a PFA dispersion having a weight of about 1gram, thereby resulting in about 2% of CNT in PFA. Prior to coating, theCNT/PFA dispersion was sonicated for about 1 min, and uniformly coatedon the glass slide.

Example 3 Preparation of SiC Filler Suspension

The SiC particles (e g., about 0.5 micron in size) were dispersed in 1%aminopropylsilane (APS) aqueous solution. APS was used as an exemplarysurface treatment agent to facilitate the dispersing of the SiCparticles. The resulting dispersion was sonicated for about 1 min forobtaining a uniform dispersion.

Example 4 Preparation of CNT/PFA/SiC Dispersion

About 6.6 gram of the mixture of CNT/polyallylamine dispersion preparedfrom the example 1, and about 3 gram of the SiC dispersion prepared fromthe example 3 were mixed with about 4.65 gram PFA dispersion, therebyresulting in about 2 wt % of CNT and 5 wt % SIC in PFA. The coatingcomposition was also sonicated for 1 min, and uniformly coated on theglass slide.

Example 5 Preparation of Fuser Member Having CNT/PFA Topcoat

The fuser member was constructed with a metal insert or substrate,preferably aluminum, but possibly including steel. To form the siliconelayer, Toray DY35-6072 silicone was applied to the substrate viamolding, post-cured, ground, and cleaned. The silicone layer was adheredto the substrate or base of the fuser roll using an adhesive, DowCorningP5200. The resulting silicone layer had a thickness of about 0.05-7 mm,and in some cases, about 0.22 mm. An aminosilane adhesive layer wasapplied to the surface of the silicone layer. A base fluoropolymer layerwas then applied to the surface of the aminosilane adhesive layer. Thisfluoropolymer layer was formed from DuPont 855-021 (from E.I. DuPont deNemours and Co), which contains polytetrafluoroethylene, fluorinatedethylene propylene resin and polyamide-imide polymer in solvent. Thisbase-coat layer was applied by spray-coating at a thickness ofapproximately 3-5 micrometers. An outer surface CNT/PFA layer was thenapplied on the base-coat fluoropolymer layer This outer surface layerwas formed from CNT/PFA, or CNT/PFA/SiC coating composition described inExample 2 and 4. This layer was applied by spray coating at anapproximate thickness of about 20-25 micrometers. The coating layer wasthen baked at about 350° C. for about 20 min and about 360° C. for about10 min. The dried coatings were uniform. The electrical resistivity wasmeasured to be about 1.0×10³ to about 1.0×10⁵ Ω/sq.

Example 6 Preparation of Fuser Member Having CNT/PFA Topcoat

The coating composition, including CNT/PFA, or CNT/PFA/SiC, was coatedon a metal fuser roll by spray-coating. The coating was then baked atabout 350° C. for about 20 min and about 360° C. for about 10 min. Thedried coatings were uniform. The electrical resistivity was measured tobe about 1.0×10³ to about 1.0×10⁴ Ω/sq.

Other embodiments of the invention will be apparent to those skilled inthe art from consideration of the specification and practice of theinvention disclosed herein. It is intended that the specification andexamples be considered as exemplary only, with a true scope and spiritof the invention being indicated by the following claims.

What is claimed is:
 1. A coated article comprising: a substrate, and acoated layer disposed over the substrate and formed from a coatingcomposition applied on the substrate, the coated layer having athickness ranging from about 5 microns to about 20 microns, wherein thecoating composition comprises: a polyfluoroalkoxypolytetrafluorethylenefluoropolymer; a plurality of nanotubes dispersed in a media; and astabilizer mixed with the fluoropolymer and the plurality of nanotubesin the media, the stabilizer being a partially neutralizedpolyallylamine polymer comprising i) an amino substituent and ii) anammonium ion substituent or salt thereof at a pH value ranging from 5 to9, the stabilizer allowing a stable dispersion of the plurality ofnanotubes in the media and in the fluoropolymer, the stabilizer having amolecular weight ranging from 300 to about 100,000, wherein the coatedarticle is one of a fuser roll, a fixing roll, a pressure roller, and arelease agent donor roll for an electrostatographic device.
 2. Thecoated article of claim 1, wherein each of the plurality of nanotubescomprises a single wall carbon nanotube (SWCNT), a multi-wall carbonnanotube (MWCNT), or the mixtures thereof.
 3. The coated article ofclaim 1, wherein each of the plurality of nanotubes has an insidediameter ranging from about 0.5 nanometer to about 20 nanometers as wellas an outside diameter ranging from about 1 nanometer to about 80nanometers, and has an aspect ratio ranging from about 1 to about 10000.4. The coated article of claim 1, wherein the media for the plurality ofnanotubes is a liquid selected from the group consisting of an alcohol,an aliphatic hydrocarbon of from C5 to about C18, an aromatichydrocarbon of from C6 to C18, an ether, a ketone, an amide, andmixtures thereof.
 5. The coated article of claim 1, wherein theplurality of nanotubes is present in an amount from about 0.01 percentto about 20 percent by weight of the fluoropolymer.
 6. The coatedarticle of claim 1, wherein the fluoropolymer is in a form of colloiddispersion, latex, suspension, or mixtures thereof.
 7. The coatedarticle of claim 1, wherein the fluoropolymer is in a form of a particledispersion with an average overall particle size ranging from about 10nanometers to about 5000 nanometers.
 8. The coated article of claim 1,further comprising one or more filler particles, the filler particlescomprising metal oxides, silicon carbide, boron nitride, or graphite,wherein the metal oxides are selected from the group consisting ofsilicon oxide, aluminum oxide, zirconium oxide, zinc oxide, tin oxide,iron oxide, magnesium oxide, manganese oxide, nickel oxide, copperoxide, antimony pentoxide, indium tin oxide, and mixtures thereof. 9.The coated article of claim 1, comprising, thepolyfluoroalkoxypolytetrafluorethylene fluoropolymer comprising aplurality of fluoropolymer latex particles in a concentration of about10 percent to about 50 percent by weight of the coating composition, theplurality of carbon nanotubes in a concentration of about 0.1 percent toabout 10 percent by weight of the coating composition, the partiallyneutralized polyallyamine stabilizer in a concentration of about 0.1percent to about 10 percent by weight of the coating composition, awater media of about 50 percent to about 90 percent by weight of thecoating composition, and optionally, one or more fillers of about 0.5percent to 10 percent by weight of the coating composition.
 10. Thecoated article of claim 1, wherein the fluoropolymer comprises a mixtureof a plurality of small fluoropolymer particles, having an average smallparticle size ranging from about 50 nanometers to about 500 nanometers,and a plurality of large fluoropolymer particles, having an averagelarge particle size ranging from about 1 micrometer to about 50micrometers.
 11. The coated article of claim 1, wherein the pH valueranges from 8 to
 9. 12. A coated article comprising: a substrate, and acoated layer disposed over the substrate and formed from a coatingcomposition applied on the substrate, wherein the coating compositioncomprises a polyfluoroalkoxypolytetrafluorethylene fluoropolymer, aplurality of nanotubes dispersed in a media, and a stabilizer mixed withthe fluoropolymer and the plurality of nanotubes in the media, thestabilizer being a partially neutralized polyallylamine polymercomprising i) an amino substituent and ii) an ammonium ion substituentor salt thereof at a pH value of 5 to 9, the stabilizer allowing astable dispersion of the plurality of nanotubes in the media and in thefluoropolymer, wherein the fluoropolymer comprises a mixture of aplurality of small fluoropolymer particles, having an average smallparticle size ranging from about 50 nanometers to about 500 nanometers,and a plurality of large fluoropolymer particles, having an averagelarge particle size ranging from about 1 micrometer to about 50micrometers, wherein the coated layer has a thickness ranging from about5 microns to about 20 microns, and wherein the coated article is one ofa fuser roll, a fixing roll, a pressure roller, and a release agentdonor roll for an electrostatographic device.
 13. The coated article ofclaim 12, wherein the coated layer is formed by heating at a temperatureranging from about 200° C. to about 400° C.
 14. The coated article ofclaim 12, wherein the coated layer has a surface resistivity of about10⁸ Ω /sq or less.
 15. The coated article of claim 12, wherein thesubstrate is formed of a material selected from the group consisting ofmetals, plastics, and ceramics, wherein the metals are selected from thegroup consisting of aluminum, anodized aluminum, steel, nickel, copper,and mixtures thereof, and wherein the plastics are selected from thegroup consisting of polyimides, polyester, PEEK, poly(arylene ether)s,polyam ides and mixtures thereof.
 16. The coated article of claim 12,wherein the substrate is in a form of a cylinder, a belt or a sheet. 17.The coated article of claim 12, further comprising one or morefunctional layers disposed between the substrate and the coated layer.18. The coated article of claim 12, wherein the media for the pluralityof nanotubes is a liquid selected from the group consisting of analcohol, an aliphatic hydrocarbon of from C5 to about C18, an aromatichydrocarbon of from C6 to C18, an ether, a ketone, an amide, andmixtures thereof.
 19. The coated article of claim 12, wherein the pHvalue ranges from 8 to
 9. 20. A coated article comprising: a substrate,and a coated layer disposed over the substrate and formed from a coatingcomposition applied on the substrate, the coated layer having athickness ranging from about 5 microns to about 20 microns, wherein thecoating composition comprises: a polyfluoroalkoxypolytetrafluorethylenefluoropolymer; a plurality of nanotubes dispersed in a media; and astabilizer mixed with the fluoropolymer and the plurality of nanotubesin the media, the stabilizer being a partially neutralizedpolyallylamine comprising i) an amino substituent and ii) an ammoniumion substituent or salt thereof at a pH value ranging from 5 to 9, thestabilizer allowing a stable dispersion of the plurality of nanotubes inthe media and in the fluoropolymer, wherein the coated article is one ofa fuser roll, a fixing roll, a pressure roller, and a release agentdonor roll for an electrostatographic device.
 21. The coated article ofclaim 20, comprising, the polyfluoroalkoxypolytetrafluorethylenefluoropolymer comprising a plurality of fluoropolymer latex particles ina concentration of about 10 percent to about 50 percent by weight of thecoating composition, the plurality of carbon nanotubes in aconcentration of about 0.1 percent to about 10 percent by weight of thecoating composition, the partially neutralized polyallyamine stabilizerin a concentration of about 0.1 percent to about 10 percent by weight ofthe coating composition, a water media of about 50 percent to about 90percent by weight of the coating composition, and optionally, one ormore fillers of about 0.5 percent to 10 percent by weight of the coatingcomposition.
 22. The coated article of claim 20, wherein the media forthe plurality of nanotubes is a liquid selected from the groupconsisting of an alcohol, an aliphatic hydrocarbon of from C5 to aboutC18, an aromatic hydrocarbon of from C6 to C18, an ether, a ketone, anamide, and mixtures thereof.
 23. The coated article of claim 20, whereinthe pH value ranges from 8 to 9.